Does the CO2 laser reduce bond strength in different types of ceramic brackets?

ABSTRACT OBJECTIVE: The aim of this study was to assess in vitro the influence of the CO2 laser and of the type of ceramic bracket on the shear bond strength (SBS) to enamel. METHODS: A total of 60 enamel test surfaces were obtained from bovine incisors and randomly assigned to two groups, according to the ceramic bracket used: Allure (A); Transcend (T). Each group was divided into 2 subgroups (n = 15): L, laser (10W, 3s); C, no laser, or control. Twenty-four hours after the bonding protocol using Transbond XT, SBS was tested at a crosshead speed of 0.5 mm/min in a universal testing machine. After debonding, the Adhesive Remnant Index (ARI) was evaluated at 10 x magnification and compared among the groups. Data were analyzed by one-way ANOVA, Tukey’s, Mann-Whitney’s and Kruskal-Wallis tests (α = 0.05). RESULTS: Mean SBS in MPa were: AL = 0.88 ± 0.84; AC = 12.22 ± 3.45; TL = 12.10 ± 5.11; TC = 17.71 ± 6.16. ARI analysis showed that 73% of the specimens presented the entire adhesive remaining on the tooth surfaces (score 3). TC group presented significantly higher SBS than the other groups. The lased specimens showed significantly lower bond strength than the non-lased groups for both tested brackets. CONCLUSION: CO2 laser irradiation decreased SBS values of the polycrystalline ceramic brackets, mainly Allure.

RESUMO OBJETIVO: o objetivo deste estudo foi avaliar in vitro a influência do laser de CO2 sobre a resistência ao cisalhamento da colagem (RCC) no esmalte dentário, usando diferentes tipos de braquetes cerâmicos. MÉTODOS: no total, 60 superfícies de esmalte de incisivos bovinos foram obtidas e aleatoriamente divididas em dois grupos, de acordo com o braquete cerâmico utilizado: Allure (A) e Transcend (T). Cada grupo foi dividido em dois subgrupos (n = 15): L, laser (10W, 3s); C, sem laser, ou controle. Vinte e quatro horas após a colagem dos braquetes com o sistema Transbond XT, foi realizado o teste de resistência ao cisalhamento, com velocidade de 0,5 mm/min, em máquina universal de ensaios mecânicos. Após a descolagem, o Índice de Remanescente de Adesivo (IRA) foi avaliado com aumento de 10X e comparado entre os grupos. Os dados foram analisados pelo ANOVA one-way, testes de Tukey’s, Mann-Whitney’s e Kruskal-Wallis (α = 0,05). RESULTADOS: as médias da RCC em MPa foram: AL = 0,88 ± 0,84; AC = 12,22 ± 3,45; TL = 12,10 ± 5,11; TC = 17,71 ± 6,16. A análise do IRA mostrou que 73% dos corpos de prova apresentaram todo o compósito remanescente aderido à superfície do esmalte (escore 3). O grupo TC apresentou valor significativamente maior de RCC do que os outros grupos. Os corpos de prova dos grupos com laser obtiveram valores adesivos significativamente menores do que os corpos de prova dos grupos sem laser, com ambos os tipos de braquetes. CONCLUSÃO: a irradiação com laser de CO2 diminuiu os valores de RCC dos braquetes policristalinos testados, principalmente do Allure.

In Vitro Erosive Effect of Pediatric Medicines on Deciduous Tooth Enamel

This study evaluated, in vitro, the erosive potential of pediatric liquid medicines in primary tooth enamel, depending on the exposure time. Sixty deciduous incisors were randomly assigned to 4 groups (n=15), according to the immersion solutions: guaifenesin; ferrous sulfate; salbutamol sulfate and artificial saliva. The immersion cycles in the medicines were undertaken under a 1-min agitation, which wasperformed three times daily, during 28 days. Surface microhardness was measured at 7,14, 21 and 28 days. The titratable acidity and buffering capacity of the immersion media were determined. Data were analyzed by Analysis of Variance and Tukey's test (α=0.05). Salbutamol sulfate caused a gradual loss in enamel microhardness deciduous, observed at all times (p<0.005). Exposure to guaifenesin or ferrous sulfate resulted in significant decrease of enamel microhardness only after 28 days (p<0.005). In the control group (artificial saliva), microhardness did not changed (p>0.005) at any of the studied times. Scanning Electron Microscopy (SEM) images revealed that after 28 days the surfaces clearly exhibited structural loss, which was unlike those immersed in artificial saliva. Erosion of deciduous enamel was dependent on the type of medicine and exposure time.

Este estudo avaliou, in vitro, o potencial erosivo de medicamentos líquidos pediátricos em esmalte de dentes decíduos, em função do tempo de exposição. Sessenta incisivos decíduos foram divididos aleatoriamente em 4 grupos (n=15), de acordo com a solução de imersão: guaifenesina, sulfato ferroso, sulfato de salbutamol e saliva artificial. Os ciclos de imersão nos medicamentos foram realizados sob agitação por 1 min, três vezes ao dia, durante 28 dias. As medidas de microdureza superficial foram realizadas após 7, 14, 21 e 28 dias. A acidez titulável e capacidade tampão dos meios de imersão foram determinadas. Os dados foram submetidos à Análise de Variância e teste de Tukey (α=0,05). O sulfato de salbutamol causou uma perda gradual na microdureza do esmalte decíduo, em todos os tempos verificados (p<0,005). A exposição à guaifenesina ou ao sulfato ferroso levou à diminuição significante da microdureza do esmalte, apenas após 28 dias (p<0,005). No grupo controle (saliva artificial) não houve alteração (p>0,005) da microdureza em nenhum dos tempos estudados. As imagens de microscopia eletrônica de varredura (MEV) revelaram que após 28 dias, as superfícies expostas aos medicamentos apresentaram perda estrutural, diferindo dos que foram imersos em saliva artificial. A erosão do esmalte decíduo foi dependente do tipo de medicamento e do tempo de exposição.

Clinical evaluation of the failure rate of metallic brackets bonded with orthodontic composites

The purpose of the present study was to evaluate in vivo the failure rate of metallic brackets bonded with two orthodontic composites. Nineteen patients with ages ranging from 10.5 to 38.7 years needing corrective orthodontic treatment were selected for study. The enamel surfaces from second premolars to second premolars were treated with Transbond Plus-Self Etching Primer (3M Unitek). Next, 380 orthodontic brackets were bonded on maxillary and mandibular teeth, as follows: 190 with Transbond XT composite (3M Unitek) (control) and 190 with Transbond Plus Color Change (3M Unitek) (experimental) in contralateral quadrants. The bonded brackets were light cured for 40 s, and initial alignment archwires were inserted. Bond failure rates were recorded over a six-month period. At the end of the evaluation, six bond failures occurred, three for each composite. Kaplan-Meyer method and log-rank test (Mantel-Cox) was used for statistical analysis, and no statistically significant difference was found between the materials (p=0.999). Both Transbond XT and Transbond Plus Color Change composites had low debonding rates over the study period.

O objetivo do presente estudo foi avaliar in vivo a taxa de falha de braquetes metálicos colados com dois compósitos ortodônticos. Dezenove pacientes com idades entre 10,5 e 38,7 anos, que necessitavam de tratamento ortodôntico corretivo, foram selecionados para estudo. As superfícies de esmalte de segundos pré-molares a segundos pré-molares foram tratadas com Transbond Plus Self-Etching Primer (3M Unitek). Em seguida, 380 bráquetes foram colados nos dentes superiores e inferiores, como segue: 190 com compósito Transbond XT (3M Unitek) (controle) e 190 com Transbond Plus Color Change (3M Unitek) (experimental), em quadrantes contralaterais. Os bráquetes colados foram fotopolimerizados por 40 s e arcos de alinhamento inicial foram inseridos. As taxas de insucesso na adesão foram registrados durante um período de seis meses. No final da avaliação, seis falhas de adesão ocorreram, três para cada composto. Para a análise estatística foram utilizados os testes de Kaplan-Meyer e log-rank (Mantel-Cox), e não houve diferença estatisticamente significante entre os materiais (p=0,999). Ambos compósitos, Transbond XT e Transbond Plus Color Change, tiveram baixas taxas de descolagem durante o período de estudo.

Dental care management in a child with recessive dystrophic epidermolysis bullosa

Epidermolysis bullosa (EB) is a heterogeneous group of rare genetic disorders characterized by marked fragility of the skin and mucous membranes in which vesiculobullous lesions occur in response to trauma, heat or no apparent cause. The recessive form of EB presents the greatest oral alterations including repeated blistering and scar formation leading to limited oral opening, ankyloglossia, tongue denudation, microstomia, vestibule obliteration and predisposition to oral carcinoma. Routine dental care may cause bullae formation on the lips and oral mucosa. Together with the ingestion of soft and frequently carbohydrate food, these anomalies lead to a high caries risk. This paper documents a case of a child diagnosed with recessive dystrophic epidermolysis bullosa (RDEB); describes the phases and difficulties of dental treatment and the measures that dentists and health care providers should adopt in order to provide a safe and effective dental treatment as well as earlier prevention to these patients.

Epidermólise bolhosa compreende um grupo heterogêneo de desordens genéticas raras caracterizadas pela fragilidade da pele e do tecido mucoso, nos quais surgem lesões bolhosas em resposta à injúrias traumáticas, ao calor ou até mesmo sem causa aparente. Na forma recessiva da doença, repetidos episódios de bolhas e formação de tecido cicatricial nos tecidos orais acabam por tornar a mucosa atrófica causando microstomia, anquiloglossia, desnudamento da língua e predisposição a desenvolvimento de carcinomas. Os simples cuidados rotineiros com a saúde bucal podem levar a formação das bolhas na mucosa bucal e nos lábios. A falta de higiene adequada associada a um consumo elevado de carboidratos e alimentos mais pastosos aumentam o risco de cárie nestes pacientes. Este relato documenta o caso de uma criança com diagnóstico de epidermólise bolhosa distrófica recessiva, descrevendo as dificuldades e as fases do tratamento odontológico realizado, enfatiza as medidas adotadas pelos profissionais de saúde para propiciar um tratamento seguro e efetivo, bem como a importância de se instituir um programa de prevenção bucal o mais precoce possível.

Bonding agent underneath sealant: shear bond strength to oil-contaminated

This study evaluated in vitro the shear bond strength of a resin-based pit-and-fissure sealant (Fluroshield - F) associated with either an ethanol-based (Adper Single Bond 2 - SB) or an acetone-based (Prime & Bond - PB) adhesive system under conditions of oil contamination. Mesial and distal enamel surfaces from 30 sound third molars were randomly assigned to 2 groups (n=30): I - no oil contamination; II - oil contamination. Contamination (0.25 mL during 10 s) was performed after 37 percent phosphoric acid etching with an air/oil spray. The specimens were randomly assigned to subgroups, according to the bonding protocol adopted: subgroup A - F was applied to enamel without an intermediate bonding agent layer; In subgroups B and C, SB and PB, respectively, were applied, light-cured, and then F was applied and light-cured. Shear bond strength was tested at a crosshead speed of 0.5 mm/min in a universal testing machine. Means (± SD) in MPa were: IA-11.28 (±1.84); IIA-12.02 (±1.15); IB-9.73 (±2.38); IIB-9.62 (±2.29); IC-28.30 (±1.63); and IIC-25.50 (±1.91). It may be concluded that the oil contamination affected negatively the sealant bonding to enamel and the acetone-based adhesive system (PB) layer applied underneath the sealant was able to prevent its deleterious effects to adhesion.

Este estudo avaliou in vitro a resistência ao cisalhamento (RC) de um selante resinoso [Fluroshield (F); Dentsply/Caulk] em associação com um sistema adesivo com solvente a base de etanol [Adper Single Bond 2 (SB); 3M/ESPE] ou a base de acetona [Prime & Bond (PB); 3M/ESPE] após contaminação com óleo do esmalte. Superfícies mesiais e distais de esmalte de 30 terceiros molares hígidos foram aleatoriamente alocadas em 2 grupos (n=30): I - contaminação com óleo; II - sem contaminação. A contaminação foi realizada (0,25 mL;10 s) com um jato de ar/óleo após o condicionamento do esmalte com ácido fosfórico a 37 por cento. Os espécimes foram aleatoriamente alocados em subgrupos, de acordo com a técnica adesiva empregada: A - F foi aplicado sobre o esmalte condicionado sem sistema adesivo; B - SB + F; C - PB + F. RC foi testada em uma máquina universal de ensaios (0,5 mm/min; 50 kgf) e os dados analisados por ANOVA e t-teste (α=0,01). As médias de RC em MPa foram: IA-11,28 (±1,84); IIA-12,02(±1,15); IB-9,73 (±2,38); IIB-9,62 (±2,29); IC-28,30 (±1.63); e IIC-25,50 (±1,91). Conclui-se que a contaminação com o óleo afetou a adesão do selante resinoso ao esmalte e o sistema adesivo com solvente a base de acetona (Prime & Bond) aplicado sob o selante foi capaz de impedir os efeitos deletérios da contaminação com óleo.

Surface and subsurface erosion of primary enamel by acid beverages over time

This study evaluated the influence of a cola-type soft drink and a soy-based orange juice on the surface and subsurface erosion of primary enamel, as a function of the exposure time. Seventy-five primary incisors were divided for microhardness test (n=45) or scanning electron microscopy (SEM) analysis (n=30). The specimens were randomly assigned to 3 groups: 1 - artificial saliva (control); 2 - cola-type soft drink; and 3 - soy-based orange juice. Immersion cycles in the beverages were undertaken under agitation for 5 min, 3 times a day, during 60 days. Surface microhardness was measured at 7, 15, 30, 45 and 60 days. After 60 days, specimens were bisected and subsurface microhardness was measured at 30, 60, 90, 120, 150 and 200 µm from the surface exposed. Data were analyzed by ANOVA and Tukey’s test (a=0.05). Groups 2 and 3 presented similar decrease of surface microhardness. Regarding subsurface microhardness, group 2 presented the lowest values. SEM images revealed that after 60 days the surfaces clearly exhibited structural loss, unlike those immersed in artificial saliva. It may be concluded that erosion of the surfaces exposed to the cola-type soft drink was more accentuated and directly proportional to the exposure time.

Este estudo avaliou a influência de um refrigerante a base de cola e um suco de laranja a base de soja na erosão da superfície e subsuperfície do esmalte do dente decíduo, em função do tempo de exposição. Setenta e cinco incisivos decíduos foram divididos para o teste de microdureza (n=45) ou para a análise em microscópio eletrônico de varredura (MEV) (n=30). Os espécimes foram alocados aleatoriamente em 3 grupos: I - saliva artificial (controle); II - refrigerante a base de cola; e III - suco de laranja a base de soja. Ciclos de imersão nas bebidas foram realizados sob agitação durante 5 min, 3 vezes ao dia, durante 60 dias. A microdureza superficial foi mensurada aos 7, 15, 30, 45 e 60 dias. Após 60 dias, os espécimes foram seccionados e a microdureza subsuperficial foi mensurada aos 30, 60, 90, 120, 150 e 200 μm. Os dados foram analisados pelos testes ANOVA e Tukey (α=5 por cento). Os grupos II e III apresentam uma diminuição similar da microdureza superficial. O grupo II apresentou menores valores de microdureza subsuperficial. As imagens de MEV revelaram que após 60 dias as superficies mostraram perdas de estruturas claramentes identificadas, diferentemente das superfícies imersas em saliva artificial. Pode-se concluir que a erosão das superficies expostas ao refrigerante a base de cola foi mais acentuada e diretamente proporcional ao tempo de exposição à bebida.

Oral findings and dental care in a patient with myelomeningocele: case report of a 3-year-old child

Myelomeningocele (MMC) is a congenital malformation of the neural tube that occurs in the first weeks of pregnancy. This malformation refers to the caudal non-closure of the neural tube and neural tissue exposure, which lead to neurological problems, such as hydrocephalus, motor disability, genitourinary tract and skeletal abnormalities and mental retardation. Patients with MMC have an acknowledged predisposition to latex allergy and are usually at a high caries risk and activity due to poor oral hygiene, fermentable carbon hydrate-rich diet and prolonged use of sugar-containing medications. This paper addresses the common oral findings in pediatric patients with MMC, discusses the strategies and precautions to deal with these individuals and reports the dental care to a young child diagnosed with this condition.

Mielomeningocele (MMC) representa uma malformação congênita do tubo neural que acontece nas primeiras semanas de gestação. Esta malformação refere-se ao não fechamento da coluna vertebral expondo a medula espinhal, que levará a problemas neurológicos, como hidrocefalia, dificuldades motoras, anomalias esqueléticas e do trato genito-urinário, além de retardo mental. Pacientes com MMC apresentam uma reconhecida predisposição à alergia ao latex e geralmente apresentam um alto risco e atividade de cárie dental decorrente de uma higiene oral deficiente, de uma dieta rica em carboidratos e do uso prolongado de medicamentos contendo açúcares. Este trabalho discorre sobre os achados bucais em crianças com MMC, discute as estratégias e precauções no manejo destes pacientes e descreve o tratamento odontológico de uma criança diagnosticada com esta condição.

Bond strength of a pit-and-fissure sealant associated to etch-and-rinse and self-etching adhesive systems to saliva-contaminated enamel: individual vs. simultaneous light curing

This study evaluated in vitro the shear bond strength (SBS) of a resin-based pit-and-fissure sealant [Fluroshield (F), Dentsply/Caulk] associated with either an etch-and-rinse [Adper Single Bond 2 (SB), 3M/ESPE] or a self-etching adhesive system [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] to saliva-contaminated enamel, comparing two curing protocols: individual light curing of the adhesive system and the sealant or simultaneous curing of both materials. Mesial and distal enamel surfaces from 45 sound third molars were randomly assigned to 6 groups (n=15), according to the bonding technique: I - F was applied to 37 percent phosphoric acid etched enamel. The other groups were contaminated with fresh human saliva (0.01 mL; 10 s) after acid etching: II - SB and F were light cured separately; III - SB and F were light cured together; IV - S3 and F were light cured separately; V - S3 and F were light cured simultaneously; VI - F was applied to saliva-contaminated, acid-etched enamel without an intermediate bonding agent layer. SBS was tested to failure in a universal testing machine at 0.5 mm/min. Data were analyzed by one-way ANOVA and Fisher's test (α=0.05).The debonded specimens were examined with a stereomicroscope to assess the failure modes. Three representative specimens from each group were observed under scanning electron microscopy for a qualitative analysis. Mean SBS in MPa were: I-12.28 (±4.29); II-8.57 (±3.19); III-7.97 (±2.16); IV-12.56 (±3.11); V-11.45 (±3.77); and VI-7.47 (±1.99). In conclusion, individual or simultaneous curing of the intermediate bonding agent layer and the resin sealant did not seem to affect bond strength to saliva-contaminated enamel. S3/F presented significantly higher SBS than the that of the groups treated with SB etch-and-rinse adhesive system and similar SBS to that of the control group, in which the sealant was applied under ideal dry, noncontaminated conditions.

Este estudo avaliou in vitro a resistência ao cisalhamento (RC) de um selante resinoso [Fluroshield (F), Dentsply/Caulk] em associação com um sistema adesivo de condicionamento total [Adper Single Bond 2 (SB), 3M/ESPE] ou auto-condicionante [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] após contaminação salivar do esmalte, comparando dois protocolos: fotopolimerização individual do sistema adesivo e do selante ou simultânea de ambos os materiais. Superfícies mesiais e distais de esmalte de 45 terceiros molares hígidos foram aleatoriamente alocadas em 6 grupos (n=15), de acordo com a técnica adesiva empregada: I - F foi aplicado sobre o esmalte condicionado com ácido fosfórico a 37 por cento. Os demais grupos foram contaminados com saliva (0,01 mL por 10 s) após o condicionamento ácido. II - SB e F foram fotopolimerizados separadamente; III - SB e F foram fotopolimerizados simultaneamente; IV - S3 e F foram fotopolimerizados separadamente; V - S3 e F foram fotopolimerizados simultaneamente; VI - F foi aplicado sobre o esmalte condicionado e contaminado sem sistema adesivo. RC foi testada em uma máquina universal de ensaios (0,5 mm/min; 50 kgf) e os dados analisados por ANOVA a 1 fator e teste exato de Fisher (α=0,05). As interfaces adesivas foram analisadas quanto ao padrão de fraturas em estereomicroscópio. Três espécimes de cada grupo foram analisados qualitativamente em microscópio eletrônico de varredura. As médias de RC em MPa foram: I-12,28 (±4,29); II-8,57 (±3,19); III-7,97 (±2,16); IV-12,56 (±3,11); V-11,45 (±3,77); e VI-7,47 (±1,99). Conclui-se que a fotopolimerização individual ou simultânea do sistema adesivo e do selante não afetou os valores de RC ao esmalte contaminado. S3/F apresentou RC estatisticamente maior do que os grupos tratados com o sistema adesivo etch-and-rinse SB e estatisticamente semelhante ao grupo controle, no qual o selante foi aplicado em condições ideais, na ausência de contaminação salivar.